烯丙基酚醛树脂的合成与性能研究

论文编号:HG039  论文字数:15142,页数:44

摘  要

  本文合成了不同接枝率的烯丙基酚醛树脂，并测定了所合成的烯丙基酚醛树脂的溶解度，软化点等性能指标。进而，选取接枝率为50%的烯丙基酚醛树脂按不同配比与双马来酰亚胺进行共聚改性，研究了不同的固化工艺对共聚改性树脂的力学性能（弯曲性能，冲击性能）和热稳定性能的影响。研究表明: 按不同配比使双马来酰亚胺与烯丙基酚醛树脂共聚，配比中随着烯丙基酚醛树脂含量的增加，共聚物的弯曲性能越好，但是其冲击强度有所降低。
关键词： 烯丙基酚醛树脂   双马来酰亚胺  共聚改性
 
 Study on the preparation of allyl phenolic resin
ABSTRACT
 
 This article was a synthesis of different graft allylic phenolic resin, and the determination of the synthesis of allylic phenolic resin solubility, softening point and other performance indicators. In turn, select grafting rate is 50% of the allyl phenolic resin by different proportions and BMI are copolymerization, research different curing process on copolymer resin mechanical analysis (bending properties, impact properties) and the influence of heat stability.Research shows that: by different ratios of the BMI and allyl phenolic resin copolymer, in as allyl phenolic resin content increases, copolymer of bending performance, but its impact will be less.
Keywords: allyl phenolic  bismaleimide  modification

目  录

摘  要 I
ABSTRACT II
1前言 1
1.1研究背景及意义 1
1.2文献综述 2
1.2.1酚醛树脂的改性 2
1.2.2双马来酰亚胺 7
1.2.3与烯丙基化合物共聚改性 9
1.2.4 浇铸固化 11
1.3 本论文的研究内容 11
1.3.1 论文任务 11
1.3.2 研究内容 11
2实验原理与方法 13
2.1 实验目的 13
2.2实验原理 13
2.3 实验流程 13
2.4 烯丙基酚醛树脂的制备 14
2.4.1实验药品 14
2.4.2实验装置图 14
2.4.3 实验步骤及现象 15
2.5后处理 16
2.5.1实验仪器 16
2.5.2试验装置图 17
2.5.3实验步骤 17
2.5.4 注意事项 18
2.6 改性 18
2.6.1实验仪器 18
2.6.2 预聚合实验步骤 18
2.6.3注意事项 19
2.6.4预聚物的固化 19
2.7树脂的力学性能测试 19
2.7.2试样制作步骤 20
2.7.3测试方法 21
2.8树脂的热力学性能测试 21
2.8.1TGA原理 21
2.8.2试验样品 22
2.8.3试验条件 22
2.9 红外吸收光谱测定双键含量的测定 23
3结果与讨论 24
3.1溶解度测试 24
3.2软化点的测试 24
3.3红外光谱测试 24
3.4热失重分析 31
3.5弯曲试验 32
3.6冲击试验 33
4结论 34
参考文献 35
谢  辞 37